多功能塑料低溫脆化試驗機檢查電線之塑料外殼以及硫化橡膠在低溫測試時的脆化特性。
The embrittlement of plastic case of the wire and the embrittlement of vulcanized rubber during low temperature test.
用戶可以選擇TS-BC直線性沖擊試驗方法或者TS-BT擺錘型沖擊試驗方法以滿足客戶對設備的不同需求。
The user can choose the TS-BC linear impact test method or TS-BT pendulum type impact test method to meet the customer's different needs of the equipment.
試驗時將試樣固定于夾具上，然后將試樣浸泡坐在低溫介質(zhì)中5分鐘，用2±0.2m/s的線速度沖擊試樣，zui后檢查試樣在zui低溫度是否出現(xiàn)裂紋、裂縫、小孔、以及是否完分離成碎片。
Test sample is fixed on the fixture, then soaked samples sitting in low temperature medium in 5 minutes, with 2 + 0.2 M / s line speed impact test specimens, the final inspection sample in the lowest temperature whether cracks, cracks, holes, and whether separates into pieces.
通過轉換卡盤托架底座可以連續(xù)的進行樣品測試，可以節(jié)省樣品放回原處時間，滿足很多樣品各自的測試標準。
Through the conversion of the chuck bracket base can be continuous sample test, can save the sample back in place of time, meet a lot of samples of the respective test standard.
多功能塑料低溫脆化試驗機測試標準：
Standard for testing of multi - functional plastic cryogenic Embrittlement Testing Machine:
GB/T5470-2008塑料沖擊法脆化溫度的測定
Determination of embrittlement temperature of plastic impact method
GB/T 12584-2008橡膠或塑料涂覆織物低溫沖擊試驗
Low temperature impact test for rubber or plastic coated fabrics
GB/T15256-1994硫化橡膠低溫脆性的測定（多試樣法）
Determination of low temperature brittleness of vulcanized rubber (Multi - specimen method)4
ISO 812-2011硫化橡膠或熱塑性橡膠--低溫脆性的測定
Vulcanized or thermoplastic - Determination of low temperature brittleness
BS 903 A25:1992 橡膠的物理試驗.第A25部分:低溫脆性測定
Physical tests for rubber - Determination of low temperature brittleness for part A25
ISO 974-2000塑料.沖擊脆化溫度的測定
Plastics. Determination of impact embrittlement temperature
ASTM D2137-2010撓性聚合物及其涂覆織物脆化點測試方法
Test method for brittle point of flexible polymer and its coated fabric
ASTM D746-2013用沖擊法測定塑料及彈性材料脆化溫度的試驗方法
Test method for brittle temperature of plastic and elastomeric materials by impact method
JIS K7216塑料低溫脆化測試方法
Test method for low temperature embrittlement of plastics
JIS K6261-2006硫化或熱塑性橡膠--低溫特性的測定
Vulcanized or thermoplastic - Determination of low temperature properties
JIS C3005-2000橡膠或塑料絕緣電線和電纜的試驗方法
Test method for rubber or plastics insulated wires and cable
JIS K 6723-1995增塑聚氯乙烯化合物 Polyvinyl chloride compound
●主要特點：Main features
卡盤轉換部分 Chuck conversion part
4組卡盤通過旋轉手柄時，轉換卡盤能夠啟動進入打擊測試狀態(tài)。
The 4 group of chuck by rotating the handle, the conversion can start to enter the test state against chuck
在規(guī)定的速度下，通過交替打擊錘打擊卡盤里樣品夾中的樣品。
in terms of speed, by alternay blow hammer in the sample sample clamp chuck.
試驗槽（低溫槽） Test trough (cryogenic tank)
通過利用復疊制冷系統(tǒng)可以冷卻到-80℃。
The -80 can be cooled by using the cascade refrigeration system
控制部分電子電路，設備依照給定的過程進行程序控制，是機器內(nèi)部固有的
Control part of the electronic circuit, the equipment according to the given process of the procedure control, is inherent in the machine
●技術參數(shù)：Low temperature embrittlement testing machine technical parameters - multi functional plastics
名稱Name： | 低溫脆化試驗機 Low temperature embrittlement test machine | 塑料低溫脆化試驗機 Low temperature embrittlement test machine |
型號modle： | TS-BT | TS-BC |
樣品卡盤Sample chuck： | 可以同時夾持4*5個樣品的夾具或者4*15個樣品的夾具 You can also clip 4*5 sample of the fixture or 4*15 sample of the fixture | |
沖擊錘速度Speed： | 1.4—2.4m/s | 2±0.2m/s |
沖擊錘頂部半徑范圍Impact edge radius： | 1.6±0.1mm | |
低溫槽：Cryogenic tank | 不銹鋼制造（內(nèi)部）包含攪拌器 Stainless steel (internal) contains agitator | |
熱介質(zhì)：Heat transfer medium | 主要使用無水乙醇（純度為98%） The main use of anhydrous ethanol (purity of 98%) | |
溫度范圍：Temperature range | -80℃～20℃ | |
冷卻系統(tǒng)：Cooling system | 雙極制冷 Bipolar refrigeration | |
加熱系統(tǒng)：Heating system | 1.5KW heater | |
溫度控制系統(tǒng)：Temperature control system | 數(shù)字溫度控制器/觸摸屏控制器 Digital temperature controller / touch screen controller | |
計時器：Timer | 數(shù)字式計時器 Digital timer | |
安全裝置：Safety device | 漏電電流斷路器，過熱保護器 Leakage current breaker, overheat protector | |